S7136H
特點
● 電子級玻璃纖維布增強無機陶瓷填料和碳氫類樹脂復合介質材料● 具有優異的低介電常數和介電損耗等高頻性能
● 不同頻率下穩定的介電性能
● 低的Z軸膨脹系數，優異的尺寸穩定性
應用領域
● 微帶和蜂窩基站
● 功率放大器
● 天線
● LNA/LNB
● 高頻無線通訊
● 衛星信號傳輸設備
- 產品性能
- 產品證書
- 資料下載
| Items | Method | Condition | Unit | Typical Value |
|---|---|---|---|---|
|
Dielectric Constant Process Dk |
IPC-TM-650 2.5.5.5 [1] | 10GHz/23℃ | - | 3.42±0.05 |
|
Dielectric Constant Design Dk |
Differential phase length test | A | - | 3.61 |
| Dielectric Constant | ICE 61189-2-721 (SPDR) | 10GHz/23℃ | - | 3.68±0.05 |
| Loss Tangent | IPC-TM-650 2.5.5.5 | 10GHz/23℃ | - | 0.0030 |
| IEC 61189-2-721 (SPDR) | 10GHz/23℃ | - | 0.0035 | |
| TcDk | IEC 61189-2-721 | 10GHz (-40-150℃) | ppm/℃ | +50 |
| Volume Resistivity | IPC-TM-650 2.5.17.1 | A | MΩ·cm | 1.1 x 108 |
|
Surface Resistivity |
IPC-TM-650 2.5.17.1 |
A | MΩ | 1.6 x 107 |
| Tg | IPC-TM-650 2.4.25 | DSC | ℃ | ＞280 |
| Td | ASTM D3850 | TGA (5% W.L) | ℃ | 390 |
| CTE (X/Y/Z-axis) | IPC-TM-650 2.4.24 | TMA (30-260℃) | ppm/℃ | 12/14/45 |
|
Peel Strength |
IPC-TM-650 2.4.8 | 288℃/10s | N/mm [ln/in] | 0.72 [4.11] |
| Water Absorption | IPC-TM-650 2.6.2.1 | D-24/34 | % | 0.06 |
| Thermal Conductivity | ASTM D5470 | 100℃ | W/m·K | 0.66 |
| Tensile Modulus (LW/CW) | ASTM D638 | A |
GPa |
16.1/18.5 |
| Tensile Strength (LW/CW) | ASTM D638 | A | MPa | 175/245 |
| Flexural Strength | IPC-TM-650 2.4.4 | A | MPa | 260 |
|
Flammability |
UL-94 | C-48/23/50 | Rating | V-0 |
Remarks:
1. [1] For double-sided boards, S7136H (CH1) results in a thickness increase of approximately 0.0007'' (18μm) and the Dk decreases by about 0.1 as the core thickness decreases from 0.0207'' to 0.0107''.2. All the typical values listed above are for your reference only and not intended for specification. Please contact Shengyi Technology Co., Ltd. for detailed information. All rights from this data sheet are reserved by Shengyi Technology Co., Ltd.
Remarks: C=Humidity conditioning, D=Immersion conditioning in distilled water, E=Temperature conditioning. The first digit following the letter indicates the duration of preconditioning inhours, the second digit the preconditioning temperature in ℃ and the third digit the relative humidity.