Autolad3G
特點
● 兼容無鉛制程
● 超低Z軸CTE：1.8%
● 高壓耐CAF性能及優異的耐高低溫循環性能
● 高耐熱性能
應用領域
● 車載專用電子器件
● 線束箱
● 引擎及車身ECU
- 產品性能
- 產品證書
- 資料下載
| Items | Method | Condition | Unit | Typical Value |
|---|---|---|---|---|
| Tg | 2.4.24.4 | DMA | ℃ | 200 |
|
2.4.24.3 |
TMA | 180 | ||
| 2.4.25D |
DSC |
190 | ||
| Td | 2.4.24.6 | 5% wt. loss | ℃ | 408 |
|
T288 |
2.4.24.1 | TMA | min | >60 |
| T300 |
2.4.24.1 |
TMA |
min |
>60 |
|
Thermal Stress (Unetched/Etched) |
2.4.13.1 |
288℃, 20s solder dip |
- |
Pass/Pass |
| CTE (Z-axis) | 2.4.24 | Before Tg | ppm/℃ | 35 |
| After Tg | ppm/℃ | 180 | ||
| 50-260℃ | % | 1.8 | ||
| Dissipation Constant (10GHz) | 2.5.5.5 | C-24/23/50 | - | 4.0 |
|
Dissipation Factor (10GHz) |
2.5.5.5 |
C-24/23/50 |
- | 0.013 |
| Volume Resistivity | 2.5.17.1 | E-24/125 | MΩ.cm | 5.0×106 |
|
Surface Resistivity |
2.5.17.1 |
E-24/125 | MΩ | 2.0×108 |
| Arc Resistance | 2.5.1 | D-48/50+D-0.5/23 | s | 160 |
| Dielectric Breakdown | 2.5.6 | D-48/50+D-0.5/23 | kV | 45+kV NB |
| Peel Strength (1Oz) | 2.4.8 | 288℃/10s | N/mm | 1.3 [7.43] |
| Flexural Strength (LW/CW) | 2.4.4 | A | MPa | 560/450 |
| Water Absorption | 2.6.2.1 | E-1/105+D-24/23 | % | 0.13 |
|
Flammability |
UL94 |
C-48/23/50 |
Rating |
V-0 |
| CTI | IEC60112 | A | Rating | PLC3 |
Remarks:
Remark:
1. All the typical value is based onthe 1.6mm (8*7628) specimen. The Dk and Df value is based on 57% RC.
2. All the typical value listed above isfor your reference only, please turn to Shengyi Technology Co., Ltd fordetailed information, and all rights from this data sheet are reserved by ShengyiTechnology Co., Ltd.
Explanations:C=Humidity conditioning; D=Immersion conditioning in distilled water;E=Temperature conditioning.
The figures following the letter symbolsindicate with the first digit the duration of the preconditioning in hours,with the second digit the preconditioning temperature in ℃ and with the third digit the relative humidity.